Reactan PTMEG-80
Polyether (PTMEG) prepolymer with TDI end groups for 80 Shore A elastomers.
- Low free TDI
- Low viscosity
- Long gel time
- Abrasion resistance
- High mechanical strength
- High load-bearing capacity
Description
A polyether prepolymer with TDI (toluene diisocyanate) end groups, formulated for high-performance industrial applications. Its low viscosity makes it easy to process even at lower temperatures, so the material is simpler and more efficient to handle. Its low free-TDI content reduces the risks associated with handling isocyanates. It offers excellent thermal stability and a long gel time, leaving more room for adjustments during processing.
Applications
Used to produce polyurethane elastomers with high mechanical strength and durability for rollers, wheels, mats, seals and other parts that must withstand wear and abrasion. Cured with MOCA it yields 80 Shore A elastomers; with TIPA/TMP, 50 Shore A. Its load-bearing capacity, abrasion resistance and range of achievable hardness make it a dependable choice for demanding applications.
| Property | Value | Unit |
|---|---|---|
| NCO | 3.6 ± 0.2 | % |
| Appearance at 25 °C | White solid | |
| Color, Gardner | 0–3 | |
| Viscosity at 85 °C | 1000–1500 | cP |
| Specific gravity | 1.05 |
| Parameter | Value | Unit |
|---|---|---|
| MOCA per 100 g of PTMEG‑80 | 10.5 | g |
| Mixing temperature, prepolymer | 85 | °C |
| Mixing temperature, MOCA | 110 | °C |
| Mold temperature | 100 | °C |
| Gel time at 80 °C | 18 | min |
| Post-cure at 110 °C | 16 | h |
| Property | Value | Unit |
|---|---|---|
| Hardness | 80 ± 2 | Shore A |
| Modulus at 100 % elongation | 4.3 | MPa |
| Modulus at 200 % elongation | 5.1 | MPa |
| Modulus at 300 % elongation | 6 | MPa |
| Tensile strength | 25 | MPa |
| Elongation at break | 610 | % |
| Tear strength, unnicked | 55 | kN/m |
| Tear strength, nicked | 27 | kN/m |
| Abrasion loss | 50 | mm³ |
| Compression set (22 h at 70 °C) | 45 | % |
| Specific gravity (elastomer) | 1.08 | |
| Compression modulus at 5 % | 0.76 | MPa |
| Compression modulus at 10 % | 1.3 | MPa |
| Compression modulus at 15 % | 1.7 | MPa |
| Compression modulus at 20 % | 2.7 | MPa |
| Compression modulus at 25 % | 3.5 | MPa |
Note: typical laboratory values, MOCA-cured; not to be construed as specifications.
Source: Reactan PTMEG-80 data sheet, rev. 1.0. Same axis scale for every product.
Pack sizes
Blanket with nitrogen after each use.
Storage
Keep in a cool, dry place. Blanket the container with nitrogen after each use. Avoid prolonged exposure to sunlight.
Safety
Use in an open, well-ventilated area. Avoid skin contact and, where possible, wear gloves and protective clothing. Avoid eye contact and wear safety glasses at all times. In case of contact with skin or eyes, rinse with plenty of soap and water for at least 15 minutes and seek immediate medical attention. If it gets on clothing, remove the contaminated clothing and rinse the affected area with water. If swallowed, seek immediate medical attention. Do not induce vomiting unless directed by a physician.
Disclaimer
This information is provided for guidance only. Users of this product should carry out their own tests and analyses to confirm its suitability for the intended application. The information herein is accurate to the best of our knowledge as of the date of the data sheet, but we do not warrant that it is complete or accurate. Product specifications and regulatory requirements may change over time. For product-specific details and availability, please contact us.